Nikli klassid ja keemiline koostis
| Puhas nikli klass | Ni{0}}Co | Cu | Si | Mn | C | Mg | S | Fe | Lisandid kokku | ÜRO tähistus |
| mitte vähem kui | ||||||||||
| N2 | 99.98 | 0.001 | 0.003 | .002 | .005 | .003 | .001 | .007 | .02 | |
| N4 | 99.9 | 0.015 | 0.03 | .002 | .01 | .01 | .001 | .04 | 0.1 | N02201 |
| N6 | 99.5 | 0.06 | 0.10 | .05 | .10 | .10 | .005 | .10 | 0.5 | N02200 |
| N8 | 99.0 | 0.15 | 0.15 | .20 | .20 | .10 | .015 | .30 | 1.0 | |
| DN | 99.35 | 0.06 | 0.02-0.10 | 0.05 | .02.10 | .02-.10 | .005 | .10 | 0.35 | |
| NY1 | 99.7 | 0.1 | 0.1 | - | .02 | .10 | .005 | .10 | 0.3 | |
| NY2 | 99.4 | 0.01-0.10 | 0.1 | - | - | - | 0.002-0.01 | .10 | 0.6 | |
| NY3 | 99.0 | 0.15 | 0.2 | - | 0.1 | 10 | 0.005 | .25 | 1.0 | |
| NMg0,1 | 99.6 | 0.05 | 0.02 | .05 | .05 | 0.07~0.15 | 0.005 | .07 | .40 | |
| NSI0.19 | 99.4 | 0.05 | 0.15~0.25 | .05 | .10 | .05 | 0.005 | .07 | .50 | |
Nikli korrosioonikindlus
Nikkel on eriti vastupidav leelise korrosioonile ja on suhteliselt stabiilne kõrgel temperatuuril või leegisulanud leelises, seetõttu kasutatakse seda peamiselt leelisetööstuses. Normaaltemperatuuril on tigu äärmiselt stabiilne merevees, soolalahuses ja orgaanilises keskkonnas (nagu rasvhape, fenool, fermentatsioon jne) ning ei ole vastupidav anorgaanilise happe korrosioonile ega äädikhappes ja kerges happes.