1,5 mm Ti-6Al-4V titaanisulamist laserkeevitusega liite mikrostruktuuri ja mehaaniliste omaduste uuring

Märksõnad:Ti-6Al-4V titaanisulam/ laserkeevitus / mikrostruktuur / mehaanilised omadused

Autorid: Fu Heguo, Liu Guangxin, Xie Hongzhi, Jiang Wentong jne

Shenyang Aircraft Industry Group Co., Ltd

Allikas: keevitamine ja lõikamine

Abstraktne: laserkeevituse ja pinna modifitseerimise 1,5 mm keevitamise katseTi-6Al-4V titaanisulam was carried out, and the microstructure and static properties of the joint were observed. The results show that due to the influence of different welding thermal cycles, The structure area of laser welding plus surface modification welding joint can be divided into a base metal area, heat affected area, equiaxed crystal area at the bottom of weld, and columnar crystal area at the top of the weld, there is widmanstatten structure in the weld structure, With the increase of the distance from the fusion line, the microstructure of the heat-affected zone increases ' The volume fraction decreased gradually.

Ühenduse mehaanilised omadused näitavad, et tõmbetugevus ja nihketugevus on samaväärsed mitteväärismetalliga ning minimaalne paindenurk on 35 kraadi, mis näitab, et liigendit saab rakendada inseneritöös.

Ti-6Al-4V titaanisulamist keevisliite morfoloogia

Keevistsooni mikrostruktuur

Erinevate piirkondade mikrostruktuuride morfoloogia kuumusest mõjutatud tsoonis

Ühenduse mehaaniliste omaduste katseväärtus

Ühenduse mehaaniliste omaduste keskmine väärtus